A series of Zn-Al-Li alloys with potential application in bioresorbable implants were cast, thermomechanically processed and tested. The formation of secondary phases, such as LiZn4, LiZn3Al and Al3Li, contributed to both dynamic recrystallization and grain refinement of the matrix (η-phase) during the hot-extrusion process, leading to grain sizes as small as 1.75 μm for Zn-4Al-0.6Li alloy (wt%). This alloy exhibited an ultimate tensile strength (UTS) of 451 MPa, a total elongation of 46% and a corrosion rate of 60 μm/year in simulated